From my experience, I would not recommend s110v if you don’t plan to be gentle with it.WilliamMunny wrote: ↑Wed Aug 24, 2022 10:35 amStill struggling with this vs the Manix 2 G-10 Dark Blue CPM S110V.

From my experience, I would not recommend s110v if you don’t plan to be gentle with it.WilliamMunny wrote: ↑Wed Aug 24, 2022 10:35 amStill struggling with this vs the Manix 2 G-10 Dark Blue CPM S110V.

It indeed chips if you hit other steel but i never had mine chip from anything else so can not complain on that front.Rinzler wrote: ↑Wed Aug 24, 2022 12:04 pmFrom my experience, I would not recommend s110v if you don’t plan to be gentle with it.WilliamMunny wrote: ↑Wed Aug 24, 2022 10:35 amStill struggling with this vs the Manix 2 G-10 Dark Blue CPM S110V.


That’s pretty bad, it will be a EDC. Not abused but used. Hope 204p would be a little better. Even S30V was a bit chippy for me. Think I just might be a tool steel guy give the choice.Rinzler wrote: ↑Wed Aug 24, 2022 12:04 pmFrom my experience, I would not recommend s110v if you don’t plan to be gentle with it.WilliamMunny wrote: ↑Wed Aug 24, 2022 10:35 amStill struggling with this vs the Manix 2 G-10 Dark Blue CPM S110V.
![]()