It looks like the composition of MRS 30 is similar to VG-10, but VG-10 has cobalt, while MRS-30 does not. And MRS-30 has silicon, while VG-10 doesn't.

If going with a stainless, I would rather see something like SG2, but it is expensive.

I will buy a couple of these regardless of what steel it's ...

Cruwear would be fantastic too.

Temp 2 in HAP 40 would be awesome, but I would prefer it be run harder than the 2015 sprints.

Temperance 2 is my favorite fixed blade. There is not a knife handle that fits my hand better. I would love to have one in 3v.

I would love a manix 2 XL in 15v!

The temperance 2 is a wonderful knife. My favorite knife ever. I have 3 of them.

I bought a zoomer on clearance. It's worth what I paid for it but I would be mad paying full price. It is butter knife dull and the Appleseed grind doesn't even go all the way to the edge. It has been finished with a microbevel.

There was some talk in a old thread about bringing back the temperance 1 in VG-10. I hope that is a reality.

The temperance 2 is my favorite knife. I have never used any knife that felt better in hand. It's like it was made for me. The balance is supurb and it's light enough to hike with and ...

The edge on mine was excellent.

M4, cruwear, 3v, cpm154cm, vg-10 - all wonderful to sharpen.

They are going quick!

This reminds me of a Grohmann Canadian Belt Knife. I will get one for sure.

I am shocked that these are still available. This is a steel with edge holding comparable to, or perhaps better than s110v (based on Larin's tests).

Mine takes a sharp and aggressive edge. The steel will take a fine edge if you really work at it, but I don't think that's its forte. It feels a ...

Broke down some furniture boxes with my M398 mule today. Edge holding is excellent. Definitely s110v / 10v class.

I just got my mule yesterday and put a toothy edge on it with DMT plates. It feels hard on the stones. It wouldn't surprise me if hardness was above 63 Rockwell. It sharpens hard. Like s110v, maybe worse. Not much burr, so at least that's a plus.

I have one. I wish it was bigger. The steel is meh. The design is quite nice though.

It is interesting how similar the edge holding is between these two steels. S35vn sharpens a little harder but not much. Corrosion resistance is the main difference.... Have definitely had rust and spotting on Cruwear. Never any hint of rust on s35vn in my use.

I have one of the early s110v militaries and it's a great knife. Mine feels like it's run hard. It outperforms the s110v in my manix and pm 2.

I really like the steel. I run it at a low angle (about 10 degrees per side). It makes sharpening easy with DMT stones. I just set the bevel with an extra ...

I find 10v to be a good bit more stainless. But when 10v does corrode it tends to pit. I like the way k390 sharpens better.... Takes a refined edge easier than 10v. Really they are very similar in my use. Edge holding I can't tell a difference.

For reference I have a pm2 and several K2s in 10v, and ...

I lost my rex 45 native chief. It made me sick.