chuck_roxas45 wrote:ZDP won't stain or patina worth a dang for me.

Same for me I've never seen anything i'm my zdp

Hey Jim,

You treat all of your knives like "red headed step children". ;)

Hey Drewskeez,

Where do you live? What have you cut? Do you keep it close to your skin and do you perspire? (Animals sweat, men perspire, women glow).

sal

I carry it in rfp and and live in NC. I polished the blade about ...

Has anyone else had rust show up on there xhp knives nothing major just some very small putting

Best thing to do is go on youtube and watch freehand sharpening videos you don't have to do it the exact same way that do but it will give you better idea of what to do

PS welcome to the forums

The military is my favorite knife I've has to date. As others have said out shrinks in a week or so give it a sho you'll never know if you like it till you uses one

Dose anyone know if it will be sw like the m390 mule?

Are there any other spydernuts that are excited about this one?

So I recently got a crkt ripple that has ikbs and it got me thinking crkt and zt are going to have a ball bearing knife but I would love to see a spyderco with something like ikbs and was wondering would any one else want one? Also what are the chances of this happening maybe with the tuff?

All I can say is WTF!

Dose anyone else have this on pre order or planning in getting one or 2

Most people have smart phones by now and there's a app for almost everything so why not a spyderco forum app

How do yal like this steel so far I've only base mine a little less than a week but think It take a finer edge and chips less than cpm-s30v and polished a little better. I also finder takes a little longer to reprofile maybe its at a higher Rc than most s30v

thay cant take debit and i dont have a credit card any ideas

i have a full set of dmt xxc to xxf and the uf. i finde that the uf leaves a higher polish so go frm the xxf dmt to the uf and then strop on harder steels like zdp and m4 but i finde i can skip the xxf on softer steels like aus8 or similer hope this helpg and if you can get both at some point

Senate wrote:pics pics pics! :)

I saw some in eBay

Mine will be hear tomorrow but I will be out of town hope it comes before I leave

Call Spyderco and get it replaced (or the vendor you bought it from)!!! It is too great of a tool to not have one that is perfect. Mine is perfect I guess because I've used it a lot and not noticed any problems.

Jack

I thought about sending it back but I decided to make one side a if and the ...

I recently picked up the brown and white pocket stones and thay are grate but the white was really uneven was yours flat or a little uneven

When it is smooth and polished it shows scratches and dings if you get them. G-10 is strong stuff but it scratches easily.

It will look nice but not for long if you use it like I do ;)

well i dont carey this one oftet so this one woulnot get beet on to much well not any more
ps im haveing ...

ive been giveing some thought to polishing my digicamo military
the g-10 is well worn and hase very little grip gas anyone seen this or don thid to the digicamo